Anneal & Strain

The annealing and strain points of a glass are widely used production control parameters. Changes in the annealing and strain point temperatures are indications of chemistry changes.

According to ASTM C-336 the annealing point temperature is the temperature at which a uniform fiber of glass (0.65 mm in diameter) elongates under an applied weight at a rate of 0.14 millimeters per minute while cooling in a special furnace at the rate of 4°C per minute. According to ASTM C-336 the strain point temperature is determined by extrapolation of the annealing point data and is the temperature at which the elongation rate is 0.0316 times the elongation rate observed at the annealing point.

This test is performed in an LVDT extensometer system that is manufactured by Orton. The Orton Model ANS Series has been designed to automatically monitor the elongation of the sample fiber and calculate the annealing and strain points according to the ASTM C-336 method.

(Note: If forming a fiber is not desired, is impractical, or impossible, annealing and strain point temperatures can still be determined by the Beam Bending Viscometer method, ASTM C-598.)

Contact us today: support@ortonceramic.com or Call 614-818-1330 to discuss your application.

Model ANS-800

Temperature Range
RT - 800 °C

Model ANS-1000

Temperature Range
RT - 1000 °C

View Products by Category:

 

Search
clear

FROM THE BLOG...

TempTab Brochure for the Dental Industry Announced

Verifying temperatures in your Sintering Furnace?  The August Buyers Guide of LMT magazine offers TempTab...

High Temperature Ceramics for Extreme Environments Workshop - June 18 & 19, 2019

The Ohio State University College of Engineering Department of Materials Science and Engineering...

2019 Introduction to Refractories Short Course

Orton's 2019 "Introduction to Refractories" short course is coming up in August. This course is an intensive...