ASTM C16

Standard Test Method for Load Testing Refractory Shapes at High Temperatures

A 25 psi load is applied to 9" x 4 1/2" x 2 1/2" or 3" bricks during a specified heating schedule. A minimum of two specimens per type/brand is suggested by ASTM. The percent deformation is measured on each brick after testing simultaneously in a gas-fired kiln up to 3150°F.

    PER TEST OF 2 PER TEST OF 4 EA ADD'L 24 HR HOLD
Misc. Products Less than 2000°F $730 $985 $290
Medium Duty Fireclay Schedule 1 2370°F $785 $1040 $290
High Duty Fireclay Schedule 2 2460°F $840 $1100 $290
Misc. Products 2550°F $895 $1150 $320
Super Duty Products Schedule 3 2640°F $930 $1190 $320
Misc. Products 2750°F $985 $1250 $320
Mullite, High Alumina Schedule 6 2900°F $1040 $1300 $350
Mullite, High Alumina Schedule 7 3000°F $1070 $1330 $350
Silica Brick to Failure Schedule 4 $1235 $1495 $350
Mag-Chrome Brick to Failure Schedule 5 $1235 $1495 $350
Other Temperatures and Conditions   Quote Quote Quote

 DOWNLOAD REQUEST FORM »

SIGNIFICANCE AND USE

3.1 The ability of refractory shapes to withstand prescribed loads at elevated temperatures is a measure of the high-temperature service potential of the material. By definition, refractory shapes must resist change due to high temperature; and the ability to withstand deformation or shape change when subjected to significant loading at elevated temperatures is clearly demonstrated when refractory shapes are subjected to this test method. The test method is normally run at sufficiently high temperature to allow some liquids to form within the test brick or to cause weakening of the bonding system. The result is usually a decrease in sample dimension parallel to the applied load and increase in sample dimensions perpendicular to the loading direction. Occasionally, shear fracture can occur. Since the test provides easily measurable changes in dimensions, prescribed limits can be established, and the test method has been long used to determine refractory quality. The test method has often been used in the establishment of written specifications between producers and consumers.

3.2 This test method is not applicable for refractory materials that are unstable in an oxidizing atmosphere unless means are provided to protect the specimens.

1. SCOPE

1.1 This test method covers the determination of the resistance to deformation or shear of refractory shapes when subjected to a specified compressive load at a specified temperature for a specified time.

1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

COPYRIGHT NOTICE

Extracted, with permission, from ASTM C16 Standard Test Method for Load Testing Refractory Shapes at High Temperatures, copyright ASTM International, 100 Barr Harbor Drive, West Conshohocken, PA 19428. A copy of the standard may be purchased from ASTM International, phone 610-832-9555, e-mail: service@astm.org, website: www.astm.org.

PURCHASE FULL STANDARD »

View Products by Category:

 

Search
clear

FROM THE BLOG...

Orton Welcomes New General Manager!

The Board of Trustees of the Edward Orton Jr. Ceramic Foundation announces the retirement of its General...

How Kiln Environment will affect a Pyrometric Cone

Those experienced in firing ceramics know that kiln atmosphere can have a major influence on the reaction...

TempTabs: What They Are & How They Work - Watch This Video!

TempTabs are used to measure temperature uniformity, consistency and repeatability in high temperature...