Standard Specification for Chemical-Resistant Masonry Units
Granular specimens are boiled in a sulfuric acid solution for a specified time period. The percent weight loss for two representative specimens per type/brand is determined.
This specification covers chemical-resistant masonry units, specifically, solid kiln fired bricks and tiles made from clay, shale, or mixtures thereof, suitable for indoor and outdoor use in masonry construction subjected to chemical environments. The bricks and tiles are considered to be of three types as follows: Type I, for use where low absorption and high acid resistance are not major factors; Type II, for use where lower absorption and higher acid resistance are required; and Type III, for use where minimum absorption and maximum acid resistance are required. The masonry units shall undergo tests and adhere accordingly to the following physical and chemical requirements: water absorption, warpage, surface texture, size and dimension, flexural strength, modulus of rupture, sulfuric acid solubility, and percent weight loss.
This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.
SIGNIFICANCE AND USE
4.1 The brick and tile covered herein are intended essentially for use in chemical environments where resistance to thermal shock may or may not be a consideration. The brick and tile are normally used with chemical-resistant mortars.
1.1 This specification covers solid, kiln fired brick and tile made from clay, shale, or mixtures thereof, suitable for indoor and outdoor use in masonry construction subjected to chemical environments (see Terminology C1232).
1.2 The physical and chemical properties of brick and tile differ from supplier to supplier, mainly because their composition is determined by the source of raw materials. Regardless of the differences, brick and tile are considered to be one of three types and one of two classes as follows:
1.2.1 Type I-For use where low absorption and high acid resistance are not major factors.
1.2.2 Type II-For use where lower absorption and higher acid resistance are required.
1.2.3 Type III-For use where minimum absorption and maximum acid resistance are required.
Note 1-Types I, II, and III may not differ significantly in thermal shock resistance. The suitability of a given brick, for a particular application should be determined at the time of purchase by agreement between the purchaser and the supplier.
Note 2-Types I and III were formerly designated Type "H" and "L" respectively.
1.2.4 Class S-For use in standard applications.
1.2.5 Class X-For use where a higher degree of precision and lower permissible variation in size than that permitted for Class S is required.
Extracted, with permission, from ASTM C279 Standard Specification for Chemical-Resistant Masonry Units, copyright ASTM International, 100 Barr Harbor Drive, West Conshohocken, PA 19428. A copy of the standard may be purchased from ASTM International, phone 610-832-9555, e-mail: firstname.lastname@example.org, website: www.astm.org.
FROM THE BLOG...
Orton is pleased to announce its partnership with Hot Disk of Gothenburg, Sweden representing Hot...
01/07/2021Jessica Putnam-Phillips on ClayShare
Jessica explains how Pyrometric cones help the firing process. Click here to Watch her on ClayShare...
09/03/2020Sue McLeod and Witness Cones
We ran across this recent post from Sue McLeod that explains why she uses Witness Cones in her firings. ...