Standard Test Method for Thermal Conductivity of Refractory Brick
The heat flow through a refractory is determined with a water-cooled copper calorimeter. The temperature limit of refractory must be specified, as well as the hot face or mean test temperatures desired. The maximum hot face temperature for testing is 2700°F. The specimens required are six 9" bricks or an 18" x 13.5" x 2.5" slab.
First hot face temperature specified: $1400
Each additional test temperature: $350
First mean temperature specified: $1650 Each additional test temperature: $350
The thermal conductivity of refractory brick is a property required for selecting their thermal transmission characteristics. Users select refractory brick to provide specified conditions of heat loss and cold face temperature, without exceeding the temperature limitation of the brick. This test method establishes placement of thermocouples and positioning of test specimens in the calorimeter.
This procedure must be used with Test Method C 201 and requires a large thermal gradient and steady state conditions. The results are based upon a mean temperature.
The data from this test method are suitable for specification acceptance, estimating heat loss and surface temperature, and design of multi-layer refractory construction.
The use of these data requires consideration of the actual application environment and conditions.
1.1 This test method supplements Test Method C201 and shall be used in conjunction with that test method to determine the thermal conductivity of refractory brick with the exception of insulating firebrick (use Test Method C 182), and carbon refractories. This test method is designed for refractories having a conductivity factor of not more than 200 Btu·in./h·ft2·°F (28.8 W/m·K).
Extracted, with permission, from ASTM C202 Standard Test Method for Thermal Conductivity of Refractory Brick, copyright ASTM International, 100 Barr Harbor Drive, West Conshohocken, PA 19428. A copy of the standard may be purchased from ASTM International, phone 610-832-9555, e-mail: email@example.com, website:www.astm.org.